Sharif Digital Repository

This study investigates the performance of geogrid-reinforced unbound pavement layer. In this study, geogrid was used in various layouts and numbers using three different gradation of granular materials. Light weight deflectometer (LWD) device is known as a useful tool to evaluate the stiffness of unbound pavement layers. In this study, the LWD was utilized to experimentally investigate factors affecting the performance of geogrid reinforcement, including the number of geogrids, geogrid layout, and the gradation of unbound layer. There are several parameters which affect the LWD test results including the hammer weight, the falling height, and the surface stress. The effect of these... 

This study investigates the performance of geogrid-reinforced unbound pavement layer. In this study, geogrid was used in various layouts and numbers using three different gradation of granular materials. Light weight deflectometer (LWD) device is known as a useful tool to evaluate the stiffness of unbound pavement layers. In this study, the LWD was utilized to experimentally investigate factors affecting the performance of geogrid reinforcement, including the number of geogrids, geogrid layout, and the gradation of unbound layer. There are several parameters which affect the LWD test results including the hammer weight, the falling height, and the surface stress. The effect of these... 

The purpose of this paper is to develop a mathematical solution to estimate the deformation pattern and required power in cold plate rolling using coupled stream function method and upper bound theorem. Design/methodology/approach-In the first place, an admissible velocity field and the geometry of deformation zone are derived from a new stream function. Then, the optimum velocity field is obtained by minimizing the corresponding power function. Also, to calculate the adiabatic heating during high speed rolling operations, a two-dimensional conduction-convection problem is sequentially coupled with the mechanical model. To verify the predictions, rolling experiments on aluminum plates are... 

We studied the flow stress and microstructural changes of nanostructured Al-6063 alloy produced by mechanical alloying at various temperatures and strain rates. The analysis of flow curves was performed by a constitutive equation, and the stress exponent and activation energy were determined as functions of strain. The deformation mechanisms were elaborated through microstructural observations by electron backscattering diffraction and transmission electron microscopy. Coarsening of the subgrains and grain growth upon deformation was monitored and related to the Zener–Hollomon parameter  

An ultrafine-grained Al6063/Al2O3 (0.8 vol.%, 25 nm) nanocomposite was prepared via powder metallurgy route through reactive mechanical alloying and hot powder extrusion. Scanning electron microcopy, transmission electron microscopy, and back scattered electron diffraction analysis showed that the grain structure of the nanocomposite is trimodal and composed of nano-size grains (< 0.1 μm), ultrafine grains (0.1–1 μm), and micron-size grains (> 1 μm) with random orientations. Evaluation of the mechanical properties of the nanocomposite based on the strengthening-mechanism models revealed that the yield strength of the ultrafine-grained nanocomposite is mainly controlled by the high-angle... 

Ultrafine-grained (UFG) Al6063/Al2O3 (0.8 vol%, 25 nm) nanocomposite was prepared via powdr metallurgy route. The grain structure of the nanocomposite composed of nano-size grains (< 0.1 μm), ultrafine grains (0.1-1 μm) and micron-size grains (>1 μm) with random orientations. It was found that the yield strength of the UFG nanocomposite is mainly controlled by the Orowan mechanism rather than the grain boundaries. The deformation activation energy at temperature ranges of T <300 ˚C and 300 ˚C ≤T < 450 ˚C was determined to be 74 and 264 kJ mol-1, respectively. At the higher temperatures, significant deformation softening was observed due to dynamic recrystallization of non-equilibrium grain... 

Ultrafine-grained (UFG) Al6063 alloy reinforced with 0.8 vol% nanometric alumina particles (25 nm) was prepared by reactive mechanical alloying and direct powder extrusion. Transmission electron microscopy and electron backscatter diffraction analysis showed that the grain structure of the nanocomposite composed of nanosize grains (<0.1 μm), ultrafine grains (0.1–1 μm) and micronsize grains (>1 μm) with random orientations. Mechanical properties of the material were examined at room and high temperatures by compression test. It was found that the yield strength of the UFG composite material is mainly controlled by the Orowan mechanism rather than the grain boundaries. The deformation... 

Nanostructured AA6063 (NS-Al) powder with an average grain size of ∼100 nm was synthesized by high-energy attrition milling of gas-atomized AA6063 powder followed by hot extrusion. The microstructural features of the consolidated specimen were studied by transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD) techniques and compared with those of coarse-grained AA6063 (CG-Al) produced by hot powder extrusion of gas-atomized powder (without using mechanical milling). The consolidated NS-Al alloy consisted of elongated ultrafine grains (aspect ratio of ∼2.9) and equiaxed nanostructured grains. A high fraction (∼78%) of high-angle grain boundaries with average... 

Modeling the mechanical behavior of asphalt binders and mixtures has been the subject of intensified research in recent decades. Master curves of the norm of the complex modulus |G*| in the linear viscoelastic domain are frequently used for modeling, while phase angle master curves are less frequently considered for this purpose. Therefore in this research, an empirical model is introduced for phase angle master curves of modified and neat bituminous binders. The model is based on a general form of a double-logistic (DL) mathematical function. The |GG*| master curve was then modeled using a mutual relationship between the phase angle and |GG*|. Master curves of three neat and seven modified... 

Modified bitumen enhances the performance properties of asphalt mixtures. A number of studies in the last decade have evaluated the performance properties of modified binders at different service temperatures. It is however possible to evaluate some modified binder time-temperature characteristics and performance properties through their rheological master curves. In this research, styrene butadiene styrene, ethylene vinyl acetate, polyphosphoric acid and crumb rubber were used to modify a PG58-22 base binder. Rheological master curves for |G∗| and phase angles of these binders were generated using data from the dynamic shear rheometer and bending beam rheometer at temperatures ranging from... 

Master curves of asphalt binders and mixtures have been traditionally used to evaluate their rheological behavior in the linear viscoelastic range. Different analytical models are available to describe the master curves of bituminous binders and mixtures. No models are currently considered universal for all modeling purposes. In this research, the general structure and capabilities of some of the most commonly used analytical models were investigated. Then, based on the patterns of phase angle master curves of ten neat and modified asphalt binders, four groups of master curve shapes were defined. The goodness of fit of the models for the different groups of master curves was used to develop... 

In the present work, hot workability of particulate-reinforced Al6061-20%SiC composite produced by direct hot extrusion technique was studied. Uniaxial hot compression test at various temperatures and strain rates was used and the workability behavior was evaluated from the flow curves and the attendant microstructures. It was shown that the presence of SiC particles in the soft Al6061 matrix deteriorates the hot workability. Bulging of the specimens and flow lines were observed, which indicates the plastic instability during hot working. Microstructure of the composites after hot deformation was found to be heterogeneous, i.e. the reinforcement clusters were observed at the flow lines. The... 

An ultrafine-grained Al6063/Al2 O3 (0.8vol.%, 25nm) nanocomposite was prepared via powder metallurgy route through reactive mechanical alloying and hot powder extrusion. Scanning electron microcopy, transmission electron microscopy, and back scattered electron diffraction analysis showed that the grain structure of the nanocomposite is trimodal and composed of nano-size grains (<0.1μm), ultrafine grains (0.1-1μm), and micron-size grains (>1μm) with random orientations. Evaluation of the mechanical properties of the nanocomposite based on the strengthening-mechanism models revealed that the yield strength of the ultrafine-grained nanocomposite is mainly controlled by the high-angle grain... 

Ultrafine-grained (UFG) Al6063 alloy reinforced with 0.8 vol% nanometric alumina particles (25 nm) was prepared by reactive mechanical alloying and direct powder extrusion. Transmission electron microscopy and electron backscatter diffraction analysis showed that the grain structure of the nanocomposite composed of nanosize grains (<0.1 μm), ultrafine grains (0.1-1 μm) and micronsize grains (>1 μm) with random orientations. Mechanical properties of the material were examined at room and high temperatures by compression test. It was found that the yield strength of the UFG composite material is mainly controlled by the Orowan mechanism rather than the grain boundaries. The deformation... 

The microstructure and mechanical properties of the ultra-fine grained (UFG) Al6063 alloy reinforced with nanometric aluminum oxide nanoparticles (25 nm) were investigated and compared with the coarse-grained (CG) Al6063 alloy (∼2 μm). The UFG materials were prepared by mechanical alloying (MA) under high-purity Ar and Ar-5 vol pct O2 atmospheres followed by hot powder extrusion (HPE). The CG alloy was produced by HPE of the gas-atomized Al6063 powder without applying MA. Electron backscatter diffraction under scanning electron microscopy together with transmission electron microscopy studies revealed that the microstructure of the milled powders after HPE consisted of ultra-fine grains... 

We studied the flow stress and microstructural changes of nanostructured Al-6063 alloy produced by mechanical alloying at various temperatures and strain rates. The analysis of flow curves was performed by a constitutive equation, and the stress exponent and activation energy were determined as functions of strain. The deformation mechanisms were elaborated through microstructural observations by electron backscattering diffraction and transmission electron microscopy. Coarsening of the subgrains and grain growth upon deformation was monitored and related to the Zener-Hollomon parameter  

Hot deformation behavior of Al6063 alloy produced by direct powder extrusion was studied by means of uniaxial compression test in the temperature range between 300 and 450°C and strain rate range between 0.01 and 1s -1. Electron backscatter diffraction (EBSD) technique and transmission electron microscopy (TEM) were utilized to study the microstructure of the material before and after the hot deformation. The microstructure of the extruded alloy consisted of elongated grains within a subgrain structure and small grains free of low angle grain boundaries (LAGBs). An equiaxed duplex microstructure consisting of large substructured grains and fine grains separated by high angle grain boundaries... 

A modified plastic yield function is proposed to predict the consolidation behavior of nanostructured metal powders and metal-matrix nanocomposite powders under uniaxial compaction. The validity of the model is verified for nanocrystalline Al6063 (~100nm) alloy reinforced without and with 0.8vol.% Al2O3 nanoparticles (~25nm). The plastic deformation propensity of these powders is analyzed by linear compaction equations. The yield stress of the powder compacts is shown to be influenced by the nano-scale grains and the reinforcement nanoparticles  

Nanostructured AA6063 (NS-Al) powder with an average grain size of ~100. nm was synthesized by high-energy attrition milling of gas-atomized AA6063 powder followed by hot extrusion. The microstructural features of the consolidated specimen were studied by transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD) techniques and compared with those of coarse-grained AA6063 (CG-Al) produced by hot powder extrusion of gas-atomized powder (without using mechanical milling). The consolidated NS-Al alloy consisted of elongated ultrafine grains (aspect ratio of ~2.9) and equiaxed nanostructured grains. A high fraction (~78%) of high-angle grain boundaries with average... 

In this work, nanocrystalline Al6063 composite powder reinforced with nanometric oxide ceramic particles was synthesized via an in situ solid-gas reaction during high-energy mechanical alloying under a mixture of argon-oxygen atmosphere. The effect of oxygen volume fraction on the morphological evolution and microstructural changes during mechanical alloying was studied by various analytical techniques including optical and electron microscopy, X-ray diffraction, laser particle size analysis, apparent density measurement, and microhardness test. The reactive mechanical alloying resulted in the formation of amorphous Al- and Al-Mg-Si-Fe oxides with a size range of 40-100. nm and volume...