Simple synthesis of silver doped TiO2 nanostructured layers by micro arc oxidation process is reported for the first time. The layers consisted of anatase and rutile phases whose characteristic XRD-peaks shifted toward lower diffraction angles when compared to the pure micro arc oxidized TiO 2 layers. Silver-doping was confirmed by XPS technique. The anatase phase crystalline size was determined as 27.6 and 21.8 nm for the layers grown under the voltages of 350 and 500 V. Employing a UV-Vis spectrophotometer, a red shift in the absorption edge of the layers was observed when silver was incorporated into the titania lattice  

Micro arc oxidation technique, as a facile and efficient process, was employed to grow sulfur doped titania porous layers. This research sheds light on the photocatalytic performance of the micro arc oxidized S-TiO2 nano-porous layers fabricated under pulse current. Morphological and topographical studies, performed by SEM and AFM techniques, revealed that increasing the frequency and/or decreasing the duty cycle resulted in formation of finer pores and smoother surfaces. XRD and XPS results showed that the layers consisted of anatase and rutile phases whose fraction was observed to change depending on the synthesis conditions. The highest anatase relative content was obtained at the... 

V2O5-TiO2 nanostructured porous layers were grown through micro arc oxidation of titanium in vanadate containing electrolytes. This study sheds light on the effect of the electric current type on the photocatalytic performance of the layers. Surface morphology of the layers was investigated by SEM. The results revealed a porous structure with a pores size of 30-180 nm depending on the frequency and the duty cycle. A uniform porous structure was obtained under the pulse-DC regime. Topographical investigations revealed a rough surface which is favorable for catalytic applications. Our XRD and XPS results showed that the layers consisted of anatase, rutile, and vanadium oxide phases whose... 

Very recently, we fabricated (WO3)x-(TiO 2)1-x layers via micro-arc oxidation process under different applied voltages. Morphological and topographical studies, accomplished by SEM and AFM techniques, revealed that the pores size as well as the surface roughness increased with the voltage. Phase structure and chemical composition of the layers were also investigated by XRD and XPS and the results showed the grown layers consisted of titanium and tungsten oxides. It was found that WO3 dispersed in the TiO2 matrix and also doped into the TiO2 lattice. In addition, optical properties of the synthesized layers were studied employing a UV-vis spectrophotometer. Band gap energy of the layers was... 

TiO2 layers were grown via pulse type microarc oxidation process under different applied voltages, frequencies, and duty cycles. Surface chemical composition and phase structure of the synthesized layers were studied utilizing X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD). Furthermore, scanning electron microscope (SEM) and atomic force microscope (AFM) were employed to investigate surface morphology and topography of the layers. It was revealed that the layers had a porous structure with both anatase and rutile phases. The anatase relative content in the layers increased with the applied frequency; meanwhile, it decreased with duty cycle at low applied voltages, but... 

The spatiotemporal dynamic of salinity concentration (SC) in saline lakes is strongly dependent on the rate of water flow into the lake, water circulation, wind speed, evaporation rate, and the phenomenon of salt precipitation and dissolution. Although in-situ observations most reliably quantify water quality metrics, the spatiotemporal distribution of such data are typically limited and cannot be readily extrapolated for either long-term projections or extensive areas. Alternatively, remotely sensed imagery has facilitated less expensive and a stronger ability to estimate water quality over a wide range of spatiotemporal resolutions. This study introduces an adaptive learning model that... 

Through a fast, simple, low cost, surfactant-free and convenient microwave-assisted route, narcis-like ZnO nanostructures (10-15 nm size) with flower diameters in the range of 1-2.5 μm were synthesized. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) spectroscopy and room temperature photoluminescence (PL) measurements were used to characterize the produced ZnO nanostructures. The principle raw materials - ammonium hydroxide (NH4OH) and zinc acetate dihydrate [Zn(CH3COO)2·2H2O] - were both inexpensive. The method was fast, simple and surfactant-free capable of producing larger quantities of zinc oxide... 

In the present study, we performed hydrothermal method as a simple and efficient route for the synthesis of rutile TiO 2 nanostructures in various concentrations of lithium hydroxide solutions. TiO 2 nanopowders with average sizes of 15 and 23 nm were prepared using 4 M and 7 M LiOH solutions. X-ray diffraction analysis (XRD), transmission electron microscope (FEG-STEM), scanning electron microscopy (SEM), and Brunauer-Emmet-Teller (BET) analyses were used in order to characterize the obtained products and comparison of the morphology of the powders obtained in different concentrations of LiOH solvent. It was shown that alkali solution concentration has affected the crystallinity,... 

Galvanostatic method was used to electrodeposit Fe nanostructures on platinum electrodes as catalysts. Scanning electron microscopy (SEM) revealed flower-like Fe deposits with high surface area. Carbon nanotubes were grown on flower-like Fe nanostructures by chemical vapor deposition. The structure of the synthesized carbon nanotubes was investigated by scanning electron microscopy, transmission electron microscopy, Raman spectroscopy and X-ray diffraction. According to X-ray diffraction patterns, Fe was the only detected constituent of the deposited coating. The carbon nanotubes had small wall-thickness and wide hollow core  

Analysis of cancer mutational signatures have been instrumental in identification of responsible endogenous and exogenous molecular processes in cancer. The quantitative approach used to deconvolute mutational signatures is becoming an integral part of cancer research. Therefore, development of a stand-alone tool with a user-friendly interface for analysis of cancer mutational signatures is necessary. In this manuscript we introduce CANCERSIGN, which enables users to identify 3-mer and 5-mer mutational signatures within whole genome, whole exome or pooled samples. Additionally, this tool enables users to perform clustering on tumor samples based on the proportion of mutational signatures in... 

We have studied systematically photocatalytic properties of the vertically aligned ZnO@CdS core-shell nanorods where the features were grown through a multistep procedure including sol-gel for the formation of ZnO seed layer, hydrothermal process to grow ZnO nanorods, and successive ion layer adsorption and reaction (SILAR) process to deposit CdS nanoshells onto the ZnO nanorods. Formation of the ZnO seed layer and vertically aligned ZnO nanorods (d ∼ 40 nm) with a hexagonal cross-section was confirmed by AFM and SEM imaging. Successful capping of ZnO nanorods with homogeneous CdS nanocrystallites (∼5 nm) was ascertained by HRTEM diffraction and imaging. Optical properties of the samples... 

Since ultraviolet (UV) irradiation cannot be applied for a long time in practical applications, it is necessary to develop a narrow band gap photocatalyst to decompose environmental pollutants under visible irradiation. In this research, (WO3)x-(TiO2)1-x nano-porous layers were fabricated by micro arc oxidation (MAO) and influence of the electrical current type on their physical and chemical properties was investigated. Morphological studies, performed by SEM technique, revealed that pore size and roughness decreased with the frequency and increased with the duty cycle. The pulse-grown layers had a finer structure when compared to those fabricated under direct current. XRD and XPS results... 

In this research, the effect of different amounts of Cr2O3 (2.5, 5, 7.5, and 10 wt.%) and sintering temperature (1850, 1900, and 1950 °C) on the sinterability and mechanical properties of liquid-phase sintered SiC-matrix composites was studied. First, raw materials were ground for 3 h using a planetary mill whose rotational speed was 180 rpm. The process of pressing the samples was completed using uniaxial pressing with the applied pressure of 90 MPa. Finally, the samples were sintered under an argon atmosphere at various temperatures for 1.5 h. In the end, the best sintered sample was annealed at 2000°C for 2 h. The phases, microstructure, and chemical composition of the samples were... 

WO3-TiO2 nano porous layers were synthesized by micro arc oxidation (MAO) process under different applied voltages in electrolytes containing sodium tungstate and phosphate salts with various concentrations. X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and energy dispersive X-ray spectroscopy (EDS) techniques were employed to study phase structure and chemical composition of the layers. According to our data analysis, the nano porous layers consisted of anatase, rutile, and tungsten oxide phases with a varying fraction depending on the voltage and electrolyte concentration. Moreover, it was found that WO3 not only dispersed in the TiO2 matrix, but also doped into the TiO2... 

Sulfur doped TiO2 layers containing nano/micro-sized pores were synthesized by micro-arc oxidation process. Effect of the applied voltage and the electrolyte composition on physical and chemical properties of the layers was investigated using SEM, AFM, XRD, XPS, and EDS techniques. A UV-vis spectrophotometer was also used to study optical properties of the layers. It was found that the doped layers were porous with a pore size of 40-170 nm. They consisted of anatase and rutile phases with varying fraction depending on the applied voltage and electrolyte concentration. Our XPS investigations revealed the existence of sulfur in the forms of S4+ and S6+ states which substituted Ti4+ in the... 

V2O5-TiO2 layers with a sheet-like morphology were synthesized by micro arc oxidation process for the first time. Surface morphology and topography of the layers were investigated by scanning electron microscope (SEM) and atomic force microscope (AFM). Phase structure and chemical composition of the layers were also studied by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques. It was revealed that the composite layers had a sheet-like structure average thickness of which was about 100 nm depending on the applied voltage. The layers consisted of anatase, rutile, and vanadium pentoxide phases fractions of which varied with the applied voltage. The optical properties... 

V2O5-TiO2 porous layers were synthesized via micro-arc oxidation for the first time. The effect of the applied voltage on morphology, composition, and photo-activity of the layers was investigated. The layers, which consisted of anatase, rutile, and vanadium pentoxide phases, revealed an enhanced photo-activity. About 93% of methylene blue solution was degraded on the synthesized layers after 120 min UV-irradiation with a reaction rate constant of k = 0.0228 min-1. The band gap energies of the vanadia-titania and pure titania layers were calculated as 2.56 and 3.39 eV, respectively  

In this research, the effect of applied voltage and electrolyte concentration on structure, chemical composition, optical properties, and especially photo-catalytic activity of the TiO2 layers containing micro/nano-sized pores are discussed. TiO2 layers were synthesized by micro arc oxidation (MAO) process using different electrolyte concentrations and applied voltages. Surface structure of the layers was studied by scanning electron microscope (SEM); furthermore, energy dispersive spectrophotometry (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) techniques were employed to determine phase structure and chemical composition of the layers. Photo-activity of the... 

Pure titania porous layers consisted of anatase and rutile phases, chemically and structurally suitable for catalytic applications, were grown via micro-arc oxidation (MAO). The effect of applied voltage, process time, and electrolyte concentration on surface structure, chemical composition, and especially photocatalytic activity of the layers was investigated. SEM and AFM studies revealed that pore size and surface roughness of the layers increased with the applied voltage, and the electrolyte concentration. Moreover, the photocatalytic performance of the layers synthesized at medium applied voltages was significantly higher than that of the layers produced at other voltages. About 90% of... 

Micro-arc oxidation process was used to synthesize V2O5-TiO2 porous layers for the first time. Surface morphology and topography of the layers were investigated by scanning electron microscope (SEM) and atomic force microscope (AFM). X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques were also employed to evaluate phase structure and chemical composition of the layers. It was found that the V2O5-TiO2 layers consisted of anatase, rutile, and vanadium pentoxide phases fraction of which varied with the applied voltage and the electrolyte concentration. It was also revealed that pore size and surface roughness increased with the applied voltage and the electrolyte...