The perovskite oxide BaTiO3, doped with Ge oxides oxidized methane to C2 coupled hydrocarbons. The ultraviolet-visible spectra of pure barium titanate and Ge doped BaTi(1-x) GexO3 (x=0.05 ,0.1) were compared. The pure barium titanate exhibited an ultraviolet absorption effect. The addition of GeO2 resulted in an increase in absorption of wavelength. Therefore, small amount of Ge decreased band gap energy. Oxygen is inserted by nucleophilic attack which may be considered as an acid-base process. For promoted BaTiO3 catalysts with stable cation valance, electron donation ability of lattice oxygen is parallels to its ability of adsorb and active oxygen, and decrease the chance of deep oxidation... 

The perovskite oxide BaTiO3, doped with Ge oxides oxidized methane to C2 coupled hydrocarbons. The pure barium titanate exhibited an ultraviolet absorption effect. The addition of GeO2 resulted in an increase in absorption of wavelength. Small amount of Ge decreased band gap energy. For promoted BaTiO3 catalysts with stable cation valance, electron donation ability of lattice oxygen was parallel to its ability of adsorb and active oxygen, and decreased the chance of deep oxidation of methyl radicals and C2 hydrocarbons and thus will result in an increase of C2 yield. This is an abstract of a paper presented at the 42nd Loss Prevention Symposium (New Orleans, LA 4/6-10/2008)  

The perovskite oxide BaTiO3, doped with Ge oxides oxidized methane to C2 coupled hydrocarbons. The ultraviolet-visible spectra of pure barium titanate and Ge doped BaTi(1-x)GexO3(x=0.05,0.1) were compared. The pure barium titanate exhibited an ultraviolet absorption effect. The addition of GeO2 resulted in an increase in absorption of wavelength. Therefore, small amount of Ge decreased band gap energy. Oxygen is inserted by nucleophilic attack which may be considered as an acid-base process. For promoted BaTiO3catalysts with stable cation valance, electron donation ability of lattice oxygen is parallels to its ability of adsorb and active oxygen, and decrease the chance of deep oxidation of... 

The anatase phase of titania was stabilised with physically modifying particulate sol-gel process. Two major parameters, peptisation temperature and drying temperature, were identified which were responsible for retarding the anatase to rutile phase transformation, crystal growth and packing of primary particles. The critical nucleus size of transformation was controlled by natural (at 25 °C) and artificial (at 50 and 70 °C) peptisation techniques. Moreover, sintering of primary particles was controlled by cool (at 0 and 5 °C) and normal (at 25 °C) drying techniques. Fourier transform infrared spectroscopy (FT-IR) analysis confirmed that a full conversion of titanium isopropoxide is obtained... 

Nanostructured and mesoporous TiO2-Ta2O5 films and powders with various TiO2:Ta2O5 molar ratios and high specific surface area (SSA) have been prepared by a straightforward particulate sol-gel route. Titanium isopropoxide and tantalum ethoxide were used as precursors and hydroxypropyl cellulose (HPC) was used as a polymeric fugitive agent (PFA) in order to increase the SSA. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that powders contained both hexagonal δ-Ta2O5 and monoclinic β-Ta2O5 phases, as well as anatase and rutile. It was observed that Ta2O5 retarded anatase-to-rutile transformation. Furthermore, δ → β phase transformation temperature increased... 

Nanocrystalline and nanostructured TiO2-Cr2O3 thin films and powders were prepared by a facile and straightforward aqueous particulate sol-gel route at low temperature of 400°C. The prepared sols showed a narrow particle size distribution with hydrodynamic diameter in the range of 17.7 nm to 19.0 nm. Moreover, the sols were stable over 4 months, with constant zeta potential measured during this period. The effect of the Cr:Ti molar ratio on the crystallization behavior of the products was studied. X-ray diffraction (XRD) analysis revealed that the powders crystallized at low temperature of 400°C, containing anatase-TiO2, rutile-TiO2, and Cr2O3 phases, depending on the annealing temperature... 

The low temperature perovskite-type calcium titanate (CaTiO3) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route. The prepared sol had a narrow particle size distribution about 17 nm. X-ray diffraction and Fourier transform infrared spectroscopy revealed that, the synthesized powders had highly pure and crystallized CaTiO3 structure with preferable orientation growth along (1 2 1) direction at 400-800 °C. The activation energy of crystal growth was calculated 5.73 kJ/mol. Furthermore, transmission electron microscope images showed that the average crystallite size of the powders annealed at 400 °C was around 3.5... 

Nanocrystalline TiO 2-Fe 2O 3 thin films and powders were prepared by a straightforward aqueous particulate sol-gel route at the low temperature of 300 °C. Titanium(IV) isopropoxide and iron(III) chloride were used as precursors, and hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powder crystallised at the low temperature of 300 °C, containing anatase-TiO 2 and hematite-Fe 2O 3 phases. Furthermore, it was found that Fe 2O 3 retarded the anatase-to-rutile transformation up to 500 °C. The activation energies for crystallite growth of TiO 2... 

The morphological manipulation and structural characterisation of TiO 2-MgO binary system by an aqueous particulate sol-gel route were reported. Different crystal structures including pure MgTiO 3, mixtures of MgTiO 3 and TiO 2 and mixtures of MgTiO 3 and Mg 2TiO 4 were tailored by controlling Mg:Ti molar ratio and annealing temperatures as the processing parameters. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that all compounds crystallised at the low temperature of 500 °C. Furthermore, it was found that the average crystallite size of the compounds depends upon the Mg:Ti molar ratio as well as the annealing temperature, being in the range 3-5 nm at... 

Nanocrystalline TiO2-AgO thin films and powders were prepared by an aqueous particulate sol-gel route at the low temperature of 573 K (300 °C). Titanium tetraisopropoxide and silver nitrate were used as precursors, hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the phase composition of the mixed oxide depends upon the annealing temperature, being a mixture of TiO2 and AgO in the range 573 K to 773 K (300 °C to 500 °C) and a mixture of TiO2, AgO, Ag2O at 973 K (700 °C). Furthermore, one of the smallest crystallite sizes was obtained for TiO... 

Nanostructured TiO2-ZrO2 thin films and powders were prepared by a straightforward aqueous particulate sol-gel route. Titanium (IV) isopropoxide and zirconium (IV) acetate hydrate were used as precursors, and hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy revealed that the powder were crystallised at the low temperature of 500 °C, containing anatase-TiO 2 and tetragonal-ZrO2 phases. Furthermore, it was found that ZrO2 retarded the anatase-to-rutile transformation up to 900 °C. The activation energies for crystallite growth of TiO2 and ZrO2 components in... 

The low temperature perovskite-type strontium titanate (SrTiO 3) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route. The prepared sol had a narrow particle size distribution with hydrodynamic diameter of about 17 nm. X-ray diffraction (XRD) revealed that the synthesized powders had a perovskite-SrTiO 3 structure with preferable orientation growth along the (1 0 0) direction. TEM images showed that the average crystallite size of the powders annealed in the range 300-800°C was around 8 nm. FE-SEM analysis and AFM images revealed that the deposited thin films had mesoporous and nanocrystalline structure with the... 

Perovskite-type barium strontium titanate (BST) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route at room temperature. The prepared sol had a narrow particle size distribution of about 20 nm. X-ray diffraction (XRD) revealed that phase composition and preferable orientation growth of BST depended upon the annealing temperature. Transmission electron microscope (TEM) images showed that the crystallite size of the powders decreased with increasing annealing temperature from 8 nm at 25 °C down to 5 nm at 800 °C. Field emission scanning electron microscope (FE-SEM) analysis and atomic force microscope (AFM) images... 

Nanocrystalline neodymium titanium oxide thin films and powders with different phase compositions with mesoporous structure were produced by a straightforward particulate sol-gel route. The sols were prepared in various Nd:Ti molar ratios and they showed a narrow particle size distribution in the range 20-26 nm. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders contained mixtures of Nd4Ti9O24, Nd2Ti4O11, Nd3Ti4O12 for titanium dominant powders (Nd:Ti ≤ 45:60), mixtures of Nd2TiO5 and Nd2O3 for neodymium dominant powders (Nd:Ti ≥ 75:25) and pure Nd3Ti4O12 phase for equal molar ratio of Nd:Ti, depending on the annealing temperature and Nd:Ti... 

Low temperature lithium titanate compounds (i.e., Li4Ti 5O12 and Li2TiO3) with nanocrystalline and mesoporous structure were prepared by a straightforward aqueous particulate sol-gel route. The effect of Li:Ti molar ratio was studied on crystallisation behaviour of lithium titanates. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders were crystallised at the low temperature of 500 °C and the short annealing time of 1 h. Moreover, it was found that Li:Ti molar ratio and annealing temperature influence the preferable orientation growth of the lithium titanate compounds. Transmission electron microscope (TEM) images showed that the average... 

Nanocrystalline zinc titanate (ZnTiO3) thin films and powders with purity of 94% were produced at the low sintering temperature of 500 °C and the short sintering time of 1 h by a straightforward aqueous particulate sol-gel route. The effect of Zn:Ti molar ratio was studied on the crystallisation behaviour of zinc titanates. The prepared sols showed a narrow particle size distribution in the range 17-19 nm. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders contained mixtures of the rhombohedral-ZnTiO3, cubic-ZnO, cubic-Zn2TiO4 phases, as well as the anatase-TiO2 and the rutile-TiO2 depending on the sintering temperature and Zn:Ti molar ratio.... 

Nanostructured TiO2-CeO2 thin films and powders were prepared by a straightforward aqueous particulate sol-gel route. Titanium (IV) isopropoxide and cerium chloride were used as precursors, and hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. The effect of Ce:Ti molar ratio was studied on the crystallisation behaviour of the products. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders crystallised at the low temperature of 500 °C, containing anatase-TiO2, rutile-TiO2 and cubic-CeO2 phases, as well as Ti 8O15, Ti3O5 and Ce 11O20 depending on annealing temperature and Ce:Ti molar... 

Nanocrystalline nickel titanate (NiTiO3) thin films and powders with mesoporous structure were produced at the low temperature of 500 °C by a straightforward particulate sol-gel route. The sols were prepared in various Ni:Ti molar ratios. X-ray diffraction and Fourier transform infrared spectroscopy revealed that the powders contained mixtures of the NiTiO 3 and NiO phases, as well as the anatase-TiO2 and the rutile-TiO2 depending on the annealing temperature and Ni:Ti molar ratio. Moreover, it was found that Ni:Ti molar ratio influences the preferable orientation growth of the nickel titanate, being on (202) planes for the nickel dominant powders (Ni:Ti ≥ 75:25) and on (104) planes for the... 

Low-temperature perovskite-type cadmium titanate (CdTiO3) with a nanocrystalline and mesoporous structure was prepared at various Ti:Cd molar ratios by a straightforward particulate sol-gel route. The prepared sols had a narrow particle size distribution, in the range 23-26 nm. X-ray diffraction and Fourier transform infrared spectroscopy revealed that the powders contained a mixture of ilmenite-CdTiO3, perovskite-CdTiO3, anatase and rutile phases, depending on the annealing temperature and the Ti:Cd molar ratio. Perovskite-CdTiO3 was the major type obtained from cadmium-prominent powders at low temperature, whereas ilmenite-CdTiO3 was the major type obtained from titanium-prominent powders... 

A systematic comparison of single and binary metal oxide TiO2, TiO2-Er2O3 and TiO2-Ta2O5 thin film gas sensors with nanocrystalline and mesoporous microstructure, prepared by sol-gel route, was conducted. The gas sensitivity was increased by secondary phase introduction into TiO2 film via two mechanisms, firstly due to the inhibition of anatase-to-rutile transformation, since the anatase phase accommodates larger amounts of adsorbed oxygen, and secondly due to the retardation of grain growth, since the higher surface area provides more active sites for gas molecule adsorption. The binary metal oxide gas sensors exhibited a remarkable response towards low concentrations of CO and NO2 gases at...