HAp and HAp/ZrO2 composite coatings were successfully electrodepesited on 316L stainless steel substrates in the solutions containing ZrO2 particles at different concentrations. The effects of ZrO2 content on characteristics of the coatings were investigated using X-ray diffraction (XRD), Fourier transform infrared spectra (FT-IR), scanning electron microscopy (SEM) and bonding strength test. Polarization and electrochemical impedance spectroscopy measurements were carried out in order to evaluate corrosion behavior of the coatings. In-vitro test in SBF and further SEM observations were performed to examine bioactivity of the coatings. HAp/ZrO2 composite coatings showed better... 

This paper describes a solution-based technique for fabrication of varistor grade composite nanopowders. The method consists of coating major varistor dopants on the surface of the ZnO nanoparticles. As a result, a homogenous mixture of dopants and ZnO nanoparticles will be achieved. TEM results indicated that a composite layer of dopants with the average particle size of 9 nm on the surface of ZnO nanoparticles has been successfully prepared. Sintering of the coated powders was performed in temperatures as low as 850 °C and final specimens with average particle size of 900 nm and density of 98.5% were achieved. In comparison to conventional mixing, varistors prepared from coated nanopowders... 

Electricity industry is ongoing towards reregulation worldwide. Some new market issues that experienced in other commodities markets are suggested to be exercised in electricity markets. Electricity and ancillary services pricing under different schemes are such issues. Pricing mechanism can be applied via several sequential markets. A day-ahead market associated with joint energy and ancillary services dispatch is used as a benchmark for contingency reserves option pricing. This paper proposed a new methodology aimed to derive the option pricing for contingency reserves as a major part of ancillary services in restructured power systems  

Introduction: Cerebellar ataxia is a common symptom of multiple sclerosis (MS), particularly in progressive forms, where gait and balance problems are the most debilitating symptoms. Exercise training is a critical component of rehabilitation in managing equilibrium dysfunction, and stationary bicycling is a safe, feasible, and effective method to reduce the symptom. Clinical walking performance tests are typically used to assess gait in these patients. However, gait analysis technologies are more sensitive and accurate at detecting subtle and subclinical changes. The purpose of this study was to determine the changes in gait parameters in MS patients with ataxic gait after using a... 

Deep learning has received much attention as of the most powerful approaches for multimodal representation learning in recent years. An ideal model for multimodal data can reason about missing modalities using the available ones, and usually provides more information when multiple modalities are being considered. All the previous deep models contain separate modality-specific networks and find a shared representation on top of those networks. Therefore, they only consider high level interactions between modalities to find a joint representation for them. In this paper, we propose a multimodal deep learning framework (MDLCW) that exploits the cross weights between representation of... 

Purpose: The aim of this study was to compare diffusion tensor imaging (DTI) isotropic map (p-map) with current radiographically (T 2/T 2 -FLAIR) methods based on abnormal hyper-signal size and location of glioblastoma tumor using a semi-automatic approach. Materials and methods: Twenty-five patients with biopsy-proved diagnosis of glioblastoma participated in this study. T 2, T 2 -FLAIR images and diffusion tensor imaging (DTI) were acquired 1 week before radiotherapy. Hyper-signal regions on T 2, T 2 -FLAIR and DTI p-map were segmented by means of semi-automated segmentation. Manual segmentation was used as ground truth. Dice Scores (DS) were calculated for validation of semiautomatic... 

Blood vessels, especially large vessels have a greater thermal effect on freezing tissue during cryosurgery. Vascular networks act as heat sources in tissue, and cause failure in cryosurgery and reappearance of cancer. The aim of this study is to numerically simulate the effect of probe location and multiprobe on heat transfer distribution. Furthermore, the effect of nanoparticles injection is studied. It is shown that the small probes location near large blood vessels could help to reduce the necessary time for tissue freezing. Nanoparticles injection shows that the thermal effect of blood vessel in tissue is improved. Using Au, Ag and diamond nanoparticles have the most growth of ice ball... 

In this work, the effects of the surface-modified nanodiamond particles (NDs) on the barrier, rheological, mechanical and thermal properties of ethylene vinyl acetate (EVA) composites for the packaging applications were investigated. Fourier transform infrared spectroscopy, as well as thermal gravimetric analysis were employed to study the grafting of vinyltriethoxy silane (VTS) on the surface of NDs. Afterwards, EVA samples containing 0, 0.1, 0.5, 1, 1.5 and 2 wt% of surface-modified NDs were prepared by a two-stage process including the solution and injection processes. In order to evaluate the physicochemical, rheological, mechanical and thermal properties of the EVA/NDs samples, field... 

The effect of temperature, pressure and bonding time on microstructure of temperature gradient transient liquid phase (TGTLP) diffusion bonded Al7075 alloy using liquid gallium interlayer was investigated. The selected bonding method relies on using the minimum amount of liquid gallium on faying surfaces, using a very fast heating rate to reach the joining temperature and imposing a temperature gradient across the bond region. The microstructure of the diffusion bonded joints was evaluated by light optical microscopy, scanning electron microscopy and energy dispersive spectroscopy (EDS). Results show that by increasing the temperature, pressure and time of joining, a more uniform... 

A major problem in real-time packet-based communication systems, is misrouted or delayed packets which results in degraded perceived voice quality. If packets are not available on time, the packets are considered as lost. The easiest solution in a network terminal receiver is to replace silence for the duration of lost speech segments. In a high quality communication system, to avoid degradation in speech quality due to packet loss, a suitable method or algorithm is needed to replace the missing segments of speech. In this paper, we introduce an adaptive filter for replacement of lost speech segment. In this method Kalman filter as a state-space based method will be used to predict the... 

In this study, the effects of the type and content of reactive diluents on the permeation/separation of carbon dioxide/nitrogen (CO2/N2) through acrylate-terminated polyurethane (APU)-acrylate/acrylic diluent (APUA) composite membranes was investigated. A series of APUs based on poly(ethylene glycol) (PEG)-1000 g mol−1, toluene diisocyanate, and 2-hydroxyethyl methacrylate was synthesized and then diluted with several reactive diluents. The results obtained from differential scanning calorimetry (DSC) and Fourier transform infrared analyses showed that the microphase interference of hard and soft segments increased with increasing reactive diluent content. Furthermore, with increasing alkene... 

Using two techniques of thermogravimetry and differential scanning calorimetry under O2 gas atmosphere from 25 to 600°C, the thermal behavior of laboratory-produced compound lead(IV) oxide α-PbO2 was investigated. The identity of products at different stages were confirmed by XRD technique. Both techniques produced similar results supporting the same decomposition stages for the compound. Three distinct energy changes were observed, namely, two endothermic and one exothermic in DSC. The amount of ΔH for each peak is also reported. © 2008 Springer Science+Business Media, LLC  

The compound, alkaline lead acetate, Pb(CH3COO)2·PbO·H2O (ALA), was purchased from the Fluka Company. The X-ray diffraction film and SEM electron microgaph of this compound were obtained and reported in this paper for the first time. The thermal behavior of alkaline lead acetate (ALA) was studied using thermogravimetery (TGA) and Differential Scanning Calorimetery (DSC) techniques under an O2 gas atmosphere from 25 to 600°C. Four distinct energy changes associated with weight changes were observed, all of them being exothermic in the DSC results. The amount of ΔH for each peak is reported. © Sharif University of Technology  

The compound, lead hydroxide Pb6O4(OH)4, was prepared by a method used for the first time in the authors laboratory. The compound was identified by XRD and it's purity was determined by analytical methods (100%). The thermal characteristics of this compound were investigated by using a thermogravimetry (TGA). This compound was found to be stable at room temperature and at 160°C will decompose completely to produce lead (II) oxide. © Sharif University of Technology, April 2007