Synthesis and Activity Test of Dehydrogenation Catalyst for C10-C14 Paraffin
, M.Sc. Thesis Sharif University of Technology ; Baghghalha, Morteza (Supervisor)
Abstract
Dehydrogenation of C10-C14 normal paraffins on Pt/alumina catalyst is a reaction of prime importance particularly to the detergent industry for the manufacture of the active ingredients. In this thesis, the modifying effect of Zn, Li, K, and Mg on the activity and selectivity of the Pt-Sn/γ-Al2O3 dehydrogenation catalysts were investigated. The catalysts were prepared by co-impregnation, characterized by TPR, BET, SEM, EDAX and XRD techniques and tested in a tubular reactor. Zinc reduced the activity of Pt-Sn alloy and hence reduced the catalyst activity in the dehydrogenation reaction and enhanced its selectivity to normal mono olefins. The addition of Li, K, and Mg to Pt-Sn/γ-Al2O3...
Modeling Catalyst Deactivation in Dehydrogenation of Ethylbenzene to Styrene
,
M.Sc. Thesis
Sharif University of Technology
;
Baghghalha, Morteza
(Supervisor)
;
Ghotbi, Siroos
(Supervisor)
Abstract
Long-term deactivation of a commercial K-promoted Fe2O3 catalyst used in the dehydrogenation of ethylbenzene to styrene monomer was studied using thirty months of operating data of three industrial SM radial fixed bed adiabatic reactors. The Langmuir-Hinshelwood, Hougen-Watson model (LHHW) was used for reaction kinetics modeling. The kinetics of coking from ethylbenzene and styrene and the short-term deactivation function due to the quick coke formation were also considered in the model. The kinetics of long-term deactivation of the catalyst for ethylbenzene dehydrogenation to styrene between 550 and 630 °C were determined by allowing the effects of temperature and time on the catalyst...
Effect of Titanium Compounds on H-kinetics of Nanostructured Magnesium Hydride
, M.Sc. Thesis Sharif University of Technology ; Simchi, Abdolreza (Supervisor) ; Maddah Hosseini, Hamid Reza (Supervisor)
Abstract
Magnesium hydride (MgH2) is an attractive candidate for solid-state hydrogen storage applications. Scanning Electron Microscopy observations showed that during cyclic absorption and desorption considerable micro-crack was formed at the reaction interface and reduced the nucleation time. To improve the kinetic properties of MgH2 during dehydrogenation a nanostructured MgH2-10%mol TiH2-6%mol TiO2 material system was prepared by high-energy ball milling. Isothermal analysis with commercial volumetric sievert demonstrated that the addition of titanium compounds significantly improved the kinetics of dehydrogenation compared to commercial MgH2
Preparation and Physico-chemical Characterization of Titanium Dioxide Nanotubes with Electrochemical Method for Oxidative Dehydrogenation of Propane (ODHP)
, M.Sc. Thesis Sharif University of Technology ; Kazemeini, mohammad (Supervisor)
Abstract
Samples of the V2O5 catalysts supported on nanostructures of TiO2 and γ-Al2O3 were synthesized via hydrothermal method for the oxidative dehydrogenation of propane (ODHP) to propylene. The TiO2 support was utilized in both commercial microstructures and prepared nanostructures from their corresponding salts. Furthermore,the γ-Al2O3 was also prepared from two novel methods. Moreover, the vanadium catalysts supported on hybrid TiO2 and γ-Al2O3 were prepared. The performances of the prepared catalysts were subsequently examined in a fixed-bed reactor. The main products were propylene, ethylene and COx.The vanadium catalyst over TiO2 and γ-Al2O3 had the best performance under the reactor test...