During the past two decades, much attention has been paid to rechargeable lithium batteries, because they have high energy density. Glass-ceramics is a category of this material, which may be of great potential as solid electrolytes.. The object of this thesis is preparation of Li2O-TiO2-P2O5 glass, glass-ceramic and investigation their electrical behavior. Prepared Samples were investigated by Differential thermal analysis (DTA), X-ray diffraction (XRD), Scanning electron microscopy (SEM), UV-Visible spectroscopy and Electrochemical impedance spectroscopy (EIS). In this study LiTi2(PO4)3 crystals were crystallized in a glass with the composition 45Li2O-25TiO2-30P2O5 (molar ratio). According... 

The goal of the present study is to analyze the effect of CaF2 and nano-TiO2 as additives on formulation and properties of common dental glass-ceramics. To achieve the goal, a glass system based on SiO2-Al2O3-Li2O-K2O-P2O5-ZnO-ZrO2 was considered to produce glass-ceramic samples and the additives, nano-TiO2 and CaF2, with the 0.5, 1, and 1.5 %Wt was added to the system. After the melting process, the glass samples poured in the water and ferrite was produced. In the next step, the ferrite was milled and pressed. In the heat treatment step, the samples were treated in the temperature range of 650-850°C in order to gain lithium disilicate glass-ceramics. In the last step, the chemical...