Pressing and Sintering of Ce-Tzp-Al¬2o3 Nanocomposite with a High Percent of Alumina And Investigation of Sinter Condition on Morphology
, M.Sc. Thesis Sharif University of Technology ; Yoozbashizadeh, Hossein (Supervisor)
Abstract
In this project alumina-zirconia-ceria nanocomposite with 80% mol alumina (0.2Ce0.1Zr0.9O2-0.8Al2O3) was produced by solution combustion synthesis method. In the mentioned method, optimal fuel with composition of 75% urea, 25% ammonium acetate, and stoichiometric amount of glycine (0.75U-0.25AA-1G) was used. Moreover, ammonium nitrate as aid combustion was added to optimal fuel. In order to calcinations, nanopowder obtained from combustion synthesis was heated to 500°C for 1 hour and kept at this temperature for 2 hours. To complete heat treatment, the nanopowder was heated to 1150°C for 2 hours and 10 min and kept at this temperature for 2 hours. Then the specimens were pressed at pressure...