Effect of equal channel angular pressing on aging treatment of Al-7075 alloy

Shaeri, M. H ; Sharif University of Technology | 2015

309 Viewed
  1. Type of Document: Article
  2. DOI: 10.1016/j.pnsc.2015.03.005
  3. Publisher: Elsevier , 2015
  4. Abstract:
  5. The effect of aging treatment on microstructure and mechanical properties of equal channel angular pressed Al-7075 alloy was examined. Commercial Al-7075 alloy in the solid solution heat-treated condition was processed by equal channel angular pressing through route BC at both the room temperature and 120°C. Only three passes of equal channel angular pressing was possible due to the low ductility of the alloy at both temperatures. Followed by equal channel angular pressing, the specimens have been aged at 120°C for different aging times. Mechanical properties were measured by Vickers microhardness and tensile tests and microstructural observations were undertaken using transmission electron microscopy, X-ray diffractometer as well as optical microscopy. Microstructural investigations showed that ultrafine-grained materials with grain size in the range of 200-350nm and 300-500nm could be obtained after three passes of equal channel angular pressing at room temperature and 120°C, respectively. Equal channel angular pressing of solid solution heat-treated Al-7075 alloy accelerates precipitation rate and subsequently leads to a significant decrease in aging time to attain maximum mechanical properties. Furthermore, it is possible to achieve maximum mechanical properties during equal channel angular pressing at 120°C as a result of dynamic aging and formation of small n{right tail}D phase
  6. Keywords:
  7. Aging treatment ; Equal channel angular pressing ; Grain refinement ; Mechanical properties ; TEM
  8. Source: Progress in Natural Science: Materials International ; Volume 25, Issue 2 , April , 2015 , Pages 159-168 ; 10020071 (ISSN)
  9. URL: http://www.sciencedirect.com/science/article/pii/S1002007115000362