Waste ceramic powder-based geopolymer mortars: effect of curing temperature and alkaline solution-to-binder ratio

Shoaei, P ; Sharif University of Technology | 2019

814 Viewed
  1. Type of Document: Article
  2. DOI: 10.1016/j.conbuildmat.2019.116686
  3. Publisher: Elsevier Ltd , 2019
  4. Abstract:
  5. In this study, the optimum curing temperature and alkaline solution-to-binder (S:B) ratio of geopolymer mortars based on waste ceramic powder (WCP) were investigated. For this purpose, mixes with S:B ratios of 0.4–0.7 were prepared and cured at 60, 75, 90, and 105 °C. The density, compressive and flexural strengths were measured at 3, 7, 14, and 28 days. Higher S:B ratios enhanced the flow of the fresh mortar. The optimum mortar was obtained for S:B ratio of 0.6 and curing temperature of 90 °C. The SEM analysis revealed that the optimal mix had a dense matrix with minimum pores. © 2019 Elsevier Ltd
  6. Keywords:
  7. Alkaline solution-to-binder ratio ; ANOVA ; Strength properties ; Waste ceramic powder (WCP) ; Analysis of variance (ANOVA) ; Ceramic materials ; Geopolymers ; Inorganic polymers ; Mortar ; Powders ; Alkaline solutions ; Binder ratio ; Ceramic powder ; Compressive and flexural strengths ; Curing temperature ; Dense matrices ; Geopolymer mortars ; Strength property ; Curing
  8. Source: Construction and Building Materials ; Volume 227 , 2019 ; 09500618 (ISSN)
  9. URL: https://www.sciencedirect.com/science/article/abs/pii/S0950061819321026