Triboelectric nanogenerators (TENG) have been reported with attractive benefits such as adaptability, lightweight, and simple integration, are interesting for self-powered sensor design. Herein, an innovative magnetically circular layers TENG (MCL-TENG) are reported for velocity sensing and damage detection. The key role of this structure is the magnets fixed on the device, providing attractive force to move. The electrical performance of MCL-TENG under loading condition is investigated experimentally. According to the structure of the magnetic system, the MCL-TENG can effectively react to a frail striking and can be utilized to consider the speed parameters and detecting crack without the... 

An investigation into the addition of different weight percentages of Fe3O4 nanoparticles to find the optimum wt.% and its effect on the microstructure, thermal, magnetic, and electrical properties of aluminum matrix composite was conducted using the powder metallurgy method. The purpose of this research was to develop magnetic properties in aluminum. Based on the obtained results, the value of density, hardness, and saturation magnetization (Ms) from 2.33 g/cm3, 43 HV and 2.49 emu/g for Al-10 Fe3O4 reached a maximum value of 3.29 g/cm3, 47 HV and 13.06 emu/g for the Al-35 Fe3O4 which showed an improvement of 41.2%, 9.3%, and 424.5%, respectively. The maximum and minimum coercivity (Hc) was... 

The influence of indium on the properties of Cu0.5Zn0.5Fe2O4 nano ferrites synthesized by sol–gel auto-combustion technique was studied. X-ray diffraction (XRD) analysis demonstrated that pure and substituted ferrites possessed cubic spinel structure. The lattice parameter increases with the inclusion of In3+ for x ≤ 0.16 and decreases subsequently. A linear decrease in crystallite size was found as concentration of indium increased. X-ray density, strain, and dislocation density were increased as indium content increases. Hopping lengths as well as radii of A and B sites revealed increasing behavior up to x = 0.16 and decreased thereafter. The spectral bands indicated the formation of... 

The controlled and stable crystal structure, reduction in Curie temperature and semiconducting nature of oxide materials are the key factors for magnetoelectrical applications. Therefore, Co0.6Mn0.4GdxFe2-xO4 where x = 0, 0.033, 0.066 and 0.10 were synthesized to analyse the structural, morphological, magnetic, and electrical properties using a sol-gel autocombustion approach. The X-ray diffraction pattern reveals that the cubic crystallite size decreases with increasing smaller content of Gd3+ oxides without any secondary phase. Field emission scanning electron microscopy (FE-SEM) and high-resolution transmission electron microscopy (HR-TEM) study explain the complete morphology,... 

Tunable microwave absorption characteristics are highly desirable for industrial applications such as antenna, absorber, and biomedical diagnostics. Here, we report BiNdxCrxFe1-2xO3 (x = 0, 0.05, 0.10, 0.15) nanoparticles (NPs) with electromagnetic matching, which exhibit tunable magneto-optical and feasible microwave absorption characteristics for microwave absorber applications. The experimental results and theoretical calculations demonstrate the original bismuth ferrite (BFO) crystal structure, while Nd and Cr injection in the BFO structure may cause to minimize dielectric losses and enhance magnetization by producing interfacial defects in the spinel structure. Nd and Cr co-doping plays... 

In this research, polyaniline@Ba0.5Sr0.5Fe12O19@MWCNTs nanocomposite was prepared via co-precipitation and in-situ polymerization methods, respectively. Microstructural, magnetic and electromagnetic wave absorption analysis of the prepared nanocomposite were studied via XRD, FESEM, VSM and VNA. Compared with Ba0.5Sr0.5Fe12O19@MWCNTs, the microwave absorption bandwidth of the coated nanocompoite with polyaniline was significantly enhanced, which increased to approxiamately 4 GHz from 3 GHz. The effective microwave absorption performance of the Ba0.5Sr0.5Fe12O19@MWCNTs nanocomposite was attributed to increase in the interfacial polarization, improvement in impedance matching as well as porous... 

NMZ ferrites doped with rare earth having spinel composition Ni0.5Mn0.3Zn0.2X0.02Fe1.98O4, whereas X = Y, Pr and Gd were synthesized by sol gel auto-ignition method. XRD, FESEM, VSM and VNA were used to determine the phase, microstructural, magnetic and electromagnetic properties of rare earths doped NMZ ferrite. XRD analysis confirms the single phase of the rare earths doped NMZ ferrite. FESEM images shows Pr doped NMZ ferrite has less agglomerations and more porous structure as compared to NMZ and other rare earths doped NMZ ferrites. Magnetic analysis shows the enhancement in saturation magnetization and remanence with the doping of Y, Pr and Gd in NMZ ferrite. Dielectric properties were... 

NiZn nanoferrites doped with rare-earth cations having stoichiometric composition such as Ni0.5Zn0.5R0.02Fe1.98O4 (R = Tb, Pr, Ce, Gd, Y) were prepared by sol–gel technique. The same amount of Ni and Zn with constant ratio of different rare-earths ions were doped to investigate the variations in the properties. X-ray diffraction (XRD), Field emission electron microscope (FESEM), and vibrating sample magnetometer (VSM) were used to investigate the structure, morphology, and magnetic properties of rare-earth doped NiZn nanoferrites, respectively. X-ray density, bulk density, and porosity were also calculated. Phase, crystallite size, structure, d-spacing, lattice parameter, micro strain, and... 

The mixed nano-ferrites materials Cu0.6Zn0.4HoxFe2−xO4 (0.00 ≤ x ≤ 0.12) were prepared via the sol–gel auto combustion technique. The TGA curve established the annealing temperature (500 °C) for phase formation. The single exothermic peak on the DSC plot occurred at 341 °C temperature. XRD patterns of these nano ferrites verified single phase formation of the FCC cubic structure. The lattice constant a was increased from 8.4244 to 8.4419 Å and then its value decreased to 8.4319 Å. Crystallite size was found in the range of 7 to 16 nm. The surface morphology of the samples was observed from the scanning electron microscope (SEM) images. The grain size was found within the range of 90 nm to... 

NMZ ferrites doped with rare earth having spinel composition Ni0.5Mn0.3Zn0.2X0.02Fe1.98O4, whereas X = Y, Pr and Gd were synthesized by sol gel auto-ignition method. XRD, FESEM, VSM and VNA were used to determine the phase, microstructural, magnetic and electromagnetic properties of rare earths doped NMZ ferrite. XRD analysis confirms the single phase of the rare earths doped NMZ ferrite. FESEM images shows Pr doped NMZ ferrite has less agglomerations and more porous structure as compared to NMZ and other rare earths doped NMZ ferrites. Magnetic analysis shows the enhancement in saturation magnetization and remanence with the doping of Y, Pr and Gd in NMZ ferrite. Dielectric properties were... 

NiZn nanoferrites doped with rare-earth cations having stoichiometric composition such as Ni0.5Zn0.5R0.02Fe1.98O4 (R = Tb, Pr, Ce, Gd, Y) were prepared by sol–gel technique. The same amount of Ni and Zn with constant ratio of different rare-earths ions were doped to investigate the variations in the properties. X-ray diffraction (XRD), Field emission electron microscope (FESEM), and vibrating sample magnetometer (VSM) were used to investigate the structure, morphology, and magnetic properties of rare-earth doped NiZn nanoferrites, respectively. X-ray density, bulk density, and porosity were also calculated. Phase, crystallite size, structure, d-spacing, lattice parameter, micro strain, and... 

The mixed nano-ferrites materials Cu0.6Zn0.4HoxFe2−xO4 (0.00 ≤ x ≤ 0.12) were prepared via the sol–gel auto combustion technique. The TGA curve established the annealing temperature (500 °C) for phase formation. The single exothermic peak on the DSC plot occurred at 341 °C temperature. XRD patterns of these nano ferrites verified single phase formation of the FCC cubic structure. The lattice constant a was increased from 8.4244 to 8.4419 Å and then its value decreased to 8.4319 Å. Crystallite size was found in the range of 7 to 16 nm. The surface morphology of the samples was observed from the scanning electron microscope (SEM) images. The grain size was found within the range of 90 nm to... 

The influence of indium on the properties of Cu0.5Zn0.5Fe2O4 nano ferrites synthesized by sol–gel auto-combustion technique was studied. X-ray diffraction (XRD) analysis demonstrated that pure and substituted ferrites possessed cubic spinel structure. The lattice parameter increases with the inclusion of In3+ for x ≤ 0.16 and decreases subsequently. A linear decrease in crystallite size was found as concentration of indium increased. X-ray density, strain, and dislocation density were increased as indium content increases. Hopping lengths as well as radii of A and B sites revealed increasing behavior up to x = 0.16 and decreased thereafter. The spectral bands indicated the formation of... 

In this study Fe3O4/CMC magnetic nanoparticles were synthesized through co-precipitation method. Afterward, laccase from Trametes hirsuta was immobilized onto Carboxymethyl cellulose (CMC)-coated magnetic Fe3O4 nanoparticles by covalent bonding between carboxyl groups of carboxymethyl cellulose and amine group of laccases. Also, the resulted magnetic nanoparticles and immobilized laccase were characterized by Fourier-transform infrared spectroscopy (FTIR), scanning electron microscope (SEM) and dynamic light scattering (DLS) analysis. Moreover, the vital factors in enzyme immobilization, such as contact time, amount of N-hydroxysuccinimide (NHS), and the amount of nanoparticles were... 

Ceramic-magnetic nanoparticles (CMNPs) are attracting attention due to their various applications, especially in biomedical industries. Among them, spinel ferrite CMNPs have received considerable deliberations among different spinel metal oxides due to their fascinating characteristics. Spinel ferrite CMNPs are used for enhancement of the applicability of CMNPs without affecting the intrinsic advantages of iron oxide CMNPs. Spinel ferrites with doping agents have useful electrical and magnetic properties in various fields. Moreover, the replacement of metallic atoms in ferrites is promising to manipulate physical characteristics and improve their performance. Among different spinel ferrites,... 

The synergistic effect of plasmonic Au-Ag nanoparticles (NPs) on the increase of absorption band of nano-sized TiO2 and magnetic property of Fe3O4 NPs on the separation-ability of this semiconductor was applied for preparation of eight magneto-plasmonic photocatalysts for degradation of rhodamine-6G (Rh6G) in textile wastewater. The size, structure, morphology, crystallinity and optical and magnetic properties of prepared photocatalysts have been evaluated by various characterization techniques. Their photocatalytic activities were assessed under irradiation of an intense linear 405-nm laser and a continuous solar-simulated xenon lamp. The results were demonstrated that in comparison to the... 

Indium substituted Cu[sbnd]Ni nanoferrites with nominal compositions Cu 0.5 Ni 0.5 In x Fe 2-x O 4 (x = 0.00–0.32)were successfully synthesized by sol-gel auto ignition method. X-ray diffraction patterns illustrated the single phase spinel structure for x ≤ 0.24. The lattice parameter ‘a’ increased from 8.3349 to 8.3723 Å and then it decreased for x = 0.32. X-ray density increased from 5.43 to 5.79 g/cm 3 . The average crystallite sizes lie in the range 33.21–17.78 nm. The cell volume was increased from 579.03 to 586.86 Å 3 with the substitution of indium ions into the spinel lattice of copper nickel ferrites. The compositional dependence of tetrahedral and octahedral radii was explained on... 

We synthesized by electrostatic self-assembly route in basic solution Fe3O4–cysteine/RGO and Fe3O4/RGO–cysteine nanocomposites. In this method, electrostatic interaction was created via negatively charged surface of the reduced graphene oxide and reduced graphene oxide–cysteine sheets and positively charged surface of the Fe3O4 and Fe3O4–Cys nanoparticles in aqueous solution. The structural and magnetic properties of the prepared samples were analyzed by x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM), respectively. The dependences of magnetization as a function of... 

Copper (Cu) substituted Co–]Ce nanoferrites with nominal composition of Co 1-x Cu x Ce 0.05 Fe 1.95 O 4 (x = 0.00, 0.25, 0.50, 0.75, 1.00) were prepared by sol-gel route. The sintering of the Cu doped Co–]Ce nanoferrites was done at 700 °C to investigate the desired properties of the Cu doped Co–]Ce nanoferrites. The combination of transition metal (Cu) and rare earth (Ce) were employed to tailor the characteristics of the spinel ferrites. The constant ratio of rare earth and systematic doping of Cu in Co ferrite was incorporated to see the effects of these ions in spinel ferrite. FTIR, FESEM, XRD and VSM were used to study the vibrational bands, phase, morphology, structure and magnetic... 

Recently, graphene oxide and its unconventional magnetism have attracted much interest due to their novel applications in spintronics, memory chips and theranostics. Owing to the excellent biocompatibility, cellular uptake, bio-conjugation possibilities, flexible chemical modification and characteristic broad-wavelength absorbance, graphene oxide and its derivatives have been utilized as contrast agents for various imaging modalities such as photoluminescence, photoacoustic or ultrasound. Despite their suitable applications in bioimaging and due to lack of magnetic moment, graphene oxide cannot confer magnetic resonance imaging contrast without incorporating the magnetic component. Such...