Wettability is one of the most important factors which significantly influences solar still efficiency. Moreover, it determines the condensation mode, i.e., filmwise or dropwise condensation. In the present study, materials with different wettability were applied as the condensing surface to evaluate the effect of wettability on the distillate production of a single slope solar still. To compare the effects of dropwise and filmwise condensation on the condensate yield, the wettability of the condensing surface was changed by applying a nano-silicon solution according to a dip coating technique. All the experiments were conducted at three surface inclination angles. The results revealed that... 

Post-deposition annealing effects on nanomechanical properties of granular TiO2 films on soda-lime glass substrates were studied. In particular, the effects of Na diffusion on the films' mechanical properties were examined. TiO2 photocatalyst films, 330 nm thick, were prepared by dip-coating using a TiO2 sol, and were annealed between 100 °C and 500 °C. Film's morphology, physical and nanomechanical properties were characterized by atomic force microscopy, X-ray photoelectron spectroscopy, X-ray diffraction, differential thermo-gravimetric analysis, and nanoindentation. Contrary to expectations, the maximum film hardness was achieved for 300°C annealing, with a value of 0.69 ± 0.05 GPa.... 

A recently developed two-level undercut-profile substrate (2LUPS), containing two levels of plateaus connected by a curved wall with an undercut profile, enables self-forming filaments in a coated conductor during physical line-of-sight deposition of buffer and superconducting layers. In the present study, the 2LUPS concept is applied to a commercial cube-textured Ni-5at.%W tape, and the surface of the 2LUPS coated with two Gd2Zr2O7 buffer layers using chemical solution deposition is examined. Except for narrow regions near the edge of upper plateaus, the plateaus are found to be covered by strongly textured Gd2Zr2O7 buffer layers after dip coating and sintering  

The biodegradation behavior of Mg, coated by polymethyl methacrylate as well as polymethyl methacrylate (PMMA)−bioactive glass (BG) composite was investigated. Electrophoretic deposition and dip coating techniques were adopted to prepare composite coating using a suspension of different percentages of the above two chemical materials. The deposited coatings were characterized using SEM, EDS, FTIR, and water contact angle measurements. Biodegradation behavior study of the coated Mg was performed using linear polarization, impedance spectroscopy, and immersion tests in simulated body fluid. The compact and homogeneous composite coating was developed as evidenced by electron microscopy results.... 

Application of corrosion resistant coatings is one of the most widely used means of protecting steel. Zinc coated (galvanize) steel, is well known for galvanic protection of steel substrates and nowadays, particular attention has been paid to the coupling of graphene oxide (GO) with metallic materials, in order to lessen corrosion rate. In this research, an isopropanol supercritical reducing environment prepared to make zinc ions bond directly with graphene oxides, to form a button shape hybrids of ZnO-Graphene (ZnOG). The hybridized bonding between zinc and graphene oxide is confirmed by Fourier Transform Infra-Red analysis. And the morphology revealed, using a Field Emission Scanning... 

Lanthanum chromite coating occupies a noticeable position as a ceramic coating on metallic interconnects in solid oxide fuel cells because of its excellent electrical conductivity, high oxidation resistance and desirable chemical stability in both oxidizing and reducing atmospheres. In the present work, a sol-gel process based on the dip-coating technique was used to prepare dense and uniform coatings on metallic alloy for interconnect application (AISI 430 type). The effect of strontium and calcium doping into lanthanum chromite structure on electrical conductivity and oxidation behavior of the coated sample has been investigated. The oxidation behavior was evaluated by cyclic oxidation... 

In this study, zirconia antistatic coatings were synthesized by a simple dip coating sol-gel route on glass substrates, then applied to polymer-based composites to potentially improve their dust or water repellent capabilities. The coating solution contained a precursor (ZrCl4), solvent (isopropanol) and coupling agent. FTIR spectra confirmed ZrO2 and ZrO compounds in both solution and antistatic coating. FE-SEM images indicated ZrO2 fibers’ thickness was controlled by changing ZrCl4 concentration (150 g–15 g ZrCl4/l) or relative humidity (20%–60%) during coating drying. Fibers grew thicker when decreasing the former or increasing the latter. The surface electrical resistivity for all... 

Interactions between the metal interconnect and glass sealant in the solid oxide cells stack are critical to retaining the system integrity. To address this issue, in the current study, 8YSZ coating is applied on the Crofer22 APU steel via sol-gel and dip-coating method. Dense and continuous 8YSZ coatings are obtained on Crofer22 APU substrates. X-ray diffraction and Raman spectroscopy results show that both cubic and tetragonal structures of 8YSZ are formed. A glass-based sealing paste is applied on bare and 8YSZ coated Crofer22 APU steel. The interfacial compatibility and chemical stability of steel/glass and steel/8YSZ/glass joint couples are investigated using SEM and EDS line scan... 

Titanium dioxide is prepared by sol gel method from titanium tetraisopropoxide (TTIP) as precursor and likewise zinc oxide is prepared by sol gel method from zinc acetate dehydrate (ZAD) as precursor. The composite sols are prepared in three different molar ratios 90TiO2:10ZnO, 70TiO2:30ZnO and 50TiO2:50ZnO. Thin film deposition is carried out by dip coating technique. Crystal structure, surface morphology and photocatalytic activity of the prepared nanocomposite thin films are investigated. The antibacterial activity of the prepared nanocomposite thin film against E-coli ATCC 25922 bacteria is examined by placing the thin film in standard aqueous E-coli medium under UV light for 1, 2, 3 and... 

Silver-doped indium tin oxide thin films were synthesized using sol-gel dip-coating technique. The influence of different silver-dopant contents and annealing temperature on the electrical, optical, structural, and morphological properties of the films were characterized by means of four-point probe, UV-Vis spectroscopy, X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and X-ray photoelectron spectroscope (XPS). XRD analysis confirmed the formation of cubic bixbyte structure of In2O3with silver nanoparticles annealed at 350 °C. XPS analysis showed that divalent tin transformed to tetravalent tin through oxidization, and silver nanoparticles embedded into ITO... 

Abstract: This study aimed to understand the microstructural, optical, and electrical properties of tin-doped indium oxide (ITO) prepared with tetravalent and divalent tin salts. The influence of tin valence on the electrical, optical, structural, and morphological properties of the films were characterized by the mean of four-point probe, thermogravimetric analysis, differential thermal analysis (DTA), UV–Vis spectroscopy, X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and X-ray photoelectron spectroscope. XRD results revealed formation of cubic bixbyite structure of In2O3 with a small shift in major peak position toward lower angles with... 

Thin films of titanium dioxide with high surface area are prepared by sol-gel dip-coating technique. In this regards, Titania nano sols with high photocatalytic activity were prepared by dissolving titanium alkoxide in alcohol and water under acidic conditions. Photocatalytic activities of titanium dioxide thin films were measured in the presence of methylene blue. Microstructure and photocatalytic activity of the films, nanopowders and titanium dioxide sols were investigated using X-ray diffraction, scanning electron microscopy, specific surface area, zeta sizer and ultraviolet-visible spectrometry techniques. Particle size analysis of sols showed that the mean particle sizes were 15 to 128... 

(Lanthanum, Cerium)(Iron, Manganese, Cobalt, Palladium)(Oxygen)3- Perovskite catalyst was prepared by the citrate route and deposited on ceramic monoliths via dip coating procedure. The catalyst was applied on a car with XU7 motors and the amount of emission was monitored with vehicle emission test systems in Sapco company. The results were compared with the imported catalyst with noble metals such as palladium, platinum and rhodium by Iran Khodro company based on the Euro III standards. The catalysts were characterized by specific surface area measurements, scanning electron microscopy, X-ray diffraction, line scan and map. In the results, obtained in the home made sample, the amount of... 

In an attempt to reduce the oxidation and Cr evaporation rates, various protective coating layers with a nominal composition of NiCo 2-xFexO4 (x = 0, 0.5, 1) were deposited on the SUS 430 ferritic stainless steel substrate, as interconnect for solid oxide fuel cell application, by sol-gel dip coating method. Then, the coated samples were soaked at 750 C for 2.5 h in N2 and subsequently for 2.5 h in air. Phase composition and microstructure of the coatings were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Moreover, long-term isothermal oxidation experiment and area specific resistance (ASR) measurement were also carried out on the coated samples. Results...