Changes of γ′ precipitate characteristics in damaged superalloy IN738LC during different stages of rejuvenation heat treatment cycles

Hosseini, S. S ; Sharif University of Technology | 2012

834 Viewed
  1. Type of Document: Article
  2. DOI: 10.1179/1743284711Y.0000000021
  3. Publisher: 2012
  4. Abstract:
  5. The present study investigates the evolution of γ′ precipitate microstructure in a creep damaged IN738LC superalloy during different stages of rejuvenation heat treatment cycles. Dissolution of coarsened γ′ precipitates in the creep damaged alloy occurred during different solution treatments. The precipitates that did not dissolve completely during solution treatment and those formed during subsequent cooling were considered to be as remnant and cooling precipitates respectively. It was found that higher solution treatment temperatures result in lower volume fraction of remnant precipitates and further formation of cooling precipitates. Slower cooling rates after solution treatment gave the chance for the existing γ′ particles to be coarser. Moreover, aging treatment increased the volume fraction of γ′ precipitates. Double solution treatment at 1190°C/4 h/furnace coolingz1120°C/4 h/air cooling followed by aging at 845°C/24 h/air cooling dissolved nearly all the coarsened precipitates and produced a new bimodal γ′ microstructure analogous with that of the original alloy
  6. Keywords:
  7. γ′ precipitate ; Rejuvenation heat treatment ; Aging treatment ; Cooling rates ; Heat treatment cycle ; Solution treatment temperatures ; Solution treatments ; Subsequent cooling ; Superalloy IN738LC ; Cerium alloys ; Cooling ; Creep ; Endocrinology ; Heat treatment ; Microstructure ; Precipitates ; Superalloys
  8. Source: Materials Science and Technology ; Volume 28, Issue 2 , Nov , 2012 , Pages 213-219 ; 02670836 (ISSN)