Microstructure, strengthening mechanisms and hot deformation behavior of an oxide-dispersion strengthened UFG Al6063 alloy [electronic resource]

Asgharzadeh, H ; Sharif University of Technology

813 Viewed
  1. Type of Document: Article
  2. DOI: 10.1016/j.matchar.2012.10.007
  3. Abstract:
  4. An ultrafine-grained Al6063/Al2O3 (0.8 vol.%, 25 nm) nanocomposite was prepared via powder metallurgy route through reactive mechanical alloying and hot powder extrusion. Scanning electron microcopy, transmission electron microscopy, and back scattered electron diffraction analysis showed that the grain structure of the nanocomposite is trimodal and composed of nano-size grains (< 0.1 μm), ultrafine grains (0.1–1 μm), and micron-size grains (> 1 μm) with random orientations. Evaluation of the mechanical properties of the nanocomposite based on the strengthening-mechanism models revealed that the yield strength of the ultrafine-grained nanocomposite is mainly controlled by the high-angle grain boundaries rather than nanometric alumina particles. Hot deformation behavior of the material at different temperatures and strain rates was studied by compression test and compared to coarse-grained Al6063 alloy. The activation energy of the hot deformation process for the nanocomposite was determined to be 291 kJ mol− 1, which is about 64% higher than that of the coarse-grained alloy. Detailed microstructural analysis revealed that dynamic recrystallization is responsible for the observed deformation softening in the ultrafine-grained nanocomposite
  5. Keywords:
  6. Ultrafine-grained materials ; Aluminum matrix nanocomposite ; Microstructure ; Hot deformation ; Dynamic recrystallization
  7. Source: Journal of Materials Characterization ; January 2013, Volume 75, Pages 108–114