This work was carried out to investigate the effect of different Ti concentrations as a modifying agent on the microstructure and tensile properties of an in-situ Al-15 pctMg2Si composite. Cast, modified, homogenized small ingots were extruded at 753 K (480°C) at the extrusion ratio of 18:1 and ram speed of 1 mm/s. Various techniques including metallography, tensile testing, scanning electron microscopy were used to characterize the mechanical behavior, microstructural observations, fracture mechanisms of this composite. The results showed that 0.5 pctTi addition and homogenizing treatment were highly effective in modifying Mg2Si particles. The results also exhibited that the addition of Ti... 

High-bainite dual phase (HBDP) steels with 34. vol.% ferrite were subjected to tensile strains of 1%, 3%, and 5% at intermediate temperatures (150-450. °C). Mechanical behavior of pre-deformed steels was then investigated at room temperature. A maximum value for both yield stress and ultimate tensile strength was observed for pre-deformed steels. A minimum elongation was also found in the same pre-deformed specimens at the range of 250-350. °C. It was found that dynamic strain aging (DSA) plays the major role in mechanical properties of pre-strained HBDP steels. The DSA indicator parameter (DSAP) was introduced to evaluate DSA mechanism. Maxima of DSAP were likewise observed at the range of... 

In this experimental study the effect of physical and thermal properties of various FRP bars on their performance under elevated temperatures are investigated. The parameters included the bars' diameter, type of fiber, type of resin, fiber to matrix ratio, and thermal properties were studied. Moreover, ANOVA (ANalysis Of VAriance) was performed in order to investigate the contribution of each variable on the obtained results. The results showed that in addition to the temperature, the bars' diameter, type of fiber, type of resin, and thermal properties (Tg and Td) of the FRP bars have contributions to the results, while the fiber to matrix ratio was found to be an ineffective factor. It was... 

Dual-phase (DP) steels with different martensite contents were produced by subjecting a low carbon steel to various heat treatment cycles. In order to investigate the effect of dynamic strain aging (DSA) on mechanical properties, tensile specimens were deformed 3% at 300 °C. Room temperature tensile tests of specimens which deformed at 300 °C showed that both yield and ultimate tensile strengths increased, while total elongation decreased. The fatigue limit increased after pre-strain in the DSA temperature range. The effects of martensite volume fraction on mechanical properties were discussed  

AISI 4340 steel bars were heated at 900 °C for one hour, annealed at 738 °C for different durations and oil-quenched in order to obtain dual phase steels with different ferrite volume fractions. A 3% prestrain at the temperature range of 150-450 °C was then imposed to the samples, and room temperature tensile tests were carried out, afterwards. Results indicate that the maximum values for both yield and ultimate tensile strength would exist for the samples pre-strained at the temperature range of 250-300 °C. Also, a sudden drop of the ductility was observed at the mentioned temperature range. The observed behavior might be attributed to the occurrence of dynamic strain aging taken place at... 

Dual phase (DP) steels with network and fibrous martensite were produced by intercritical annealing heat treatment cycles. Some of these steels were deformed at dynamic strain aging temperatures. Room temperature tensile tests of specimens deformed at 300 °C showed that both yield and ultimate tensile strengths for both morphologies increased, while total elongation decreased. Fatigue test results before and after high temperature deformation showed that dynamic strain aging has a stronger effect on fatigue properties of dual phase steels with fibrous martensite. Cracks in DP steels with fibrous martensite propagate in a tortuous path in soft ferrite phase, while they pass of both hard and... 

4340 steel bars were austenitized at 850 °C for 1 h followed by heating at 700 °C for 90 min and quenching into a salt bath at the temperature range of 300-450 °C for 1 h to obtain dual structures with 34 vol.% fraction ferrite and various bainite morphologies. SEM studies showed that by increasing the austempering temperature, bainite morphology varies from lower to upper bainite. Tensile, impact and hardness tests revealed that increasing the austempering temperature from 300 to 400 °C leads to a reduction in yield and ultimate tensile strength, hardness, uniform and total elongation and impact energy. But in dual phase steel produced by austempering at 450 °C, yield and tensile strength... 

Low-carbon steel sheets are severely plastic deformed to strains of up to ≈3.48 and subsequently heat treated by conventional annealing followed by water-quenching. Four temperatures are chosen for the annealing below and over the Ac1 and Ac3 transformation lines. The effects of post-deformation heat treatment are investigated by evaluating the microstructure and mechanical properties, including strength, ductility, work hardening capability, and hardness. A maximum increase of 86% in the strength is obtained through intercritical annealing and quenching of the samples subjected to strain of 1.16. It is interesting that both the elongation and ultimate tensile strength values are higher... 

In this work, examinations on the microstructure and mechanical properties of plain carbon steel and AISI 430 ferritic stainless steel dissimilar welds are carried out. Welding is conducted in both autogenous and using ER309L austenitic filler rod conditions through gas tungsten arc welding process. The results indicate that fully-ferritic and duplex ferritic-martensitic microstructures are formed for autogenous and filler-added welds, respectively. Carbide precipitation and formation of martensite at ferrite grain boundaries (intergranular martensite) as well as grain growth occur in the heat affected zone (HAZ) of AISI 430 steel. It is found that weld heat input can strongly affect grain... 

Effects of Fe particle volume percent (from 0 to 5%) and changing the tool rotation direction in each pass were studied on the microstructure evolution and mechanical properties of the in situ Al/intermetallic composites produced by three passes friction stir processing (FSP) with ∼10 µm Fe particles. Optical and scanning electron microscopes were used for the investigation of the composite homogeneity, formation of Al–Fe intermetallic compounds, and fracture surfaces. Tensile and microhardness tests were also carried out to evaluate the mechanical properties of the composites. Solid-state reactions between the aluminum matrix and Fe particles led to in situ formation of Al3Fe and Al5Fe2... 

In this research, ultrahigh-molecular-weight polyethylene (UHMWPE)/multiwalled carbon nanotube (MWCNT) nanocomposites with different nanotube concentrations (0.5, 1.5, 2.5, and 3.5 wt %) were prepared via in situ polymerization with a novel, bisupported Ziegler-Natta catalytic system. Magnesium ethoxide [Mg(OEt) 2] and surface-functionalized MWCNTs were used as the support of the catalyst. Titanium tetrachloride (TiCl 4) accompanied by triethylaluminum constituted the Ziegler-Natta catalytic system. Preparation of the catalyst and the polymerization were carried out in the slurry phase under an argon atmosphere. Support of the catalyst on the MWCNTs was investigated with Fourier transform... 

The grain size of constrained groove pressed aluminum has been predicted through the genetic programming approach. “Sheet thickness,” “elongation,” “yield strength,” “ultimate tensile strength,” “total strain,” and “hardness,” along with “primary grain size” of the ultrafine-grained sheets were utilized as input parameters to obtain the ultimate grain size. A total number of 73 available data in the literature were gathered and randomly divided into 60 and 13 sets for algorithm training and testing, respectively. Among the presented models, the one with best performance utilized parameters of total strain, ultimate tensile strength, and primary grain size with 40 chromosomes, 10 head sizes,... 

In this work, the effect of hot deformation temperature on microstructure and mechanical properties of micro alloyed steel was studied. The results indicated that by decreasing the deformation temperature final microstructure is refined and the volume fraction of grain boundary ferrite is increased and some pearlite is produced. Therefore both the yield strength and ultimate tensile strength is increased, while the toughness is preserved in comparison to a ferritic-pearlitic microstructure. Also a model was developed to relate the deformation condition to the volume fraction of acicular ferrite at mixed microstructure. © 2008 Elsevier Ltd. All rights reserved  

The variation of morphology and mechanical properties of Al6061 automotive aluminum alloy due to friction stir welding (FSW) and gas tungsten arc welding (GTAW) was investigated by optical metallography, scanning electron microscopy, microhardness measurement, X-ray diffraction, tensile testing, and fractography. The center-line dendrite emergence and microhardness reduction in the heat-affected zone were observed in the GTAW process. Although similar microhardness reduction with respect to the base metal was observed in the FSW samples, higher HVs were obtained for the FSW rather than the GTAW process at almost all heat-affected locations. Ultimate tensile strengths of the FSW and the GTAW... 

Aluminum matrix in situ nanocomposite was produced by one to six passes friction stir processing (FSP) with pre-placed Fe3O4 nanoparticles (15-20 nm). Microstructure studies showed that solid-state reactions between the aluminum matrix and Fe3O4 particles during the process led to in situ formation of Al3Fe and Al5Fe2 in the stir zone. Initial Fe3O4 as well as Al-Fe intermetallic compounds (IMCs) particles were homogeneously dispersed in a fine grain matrix after six passes of FSP. Hardness and ultimate tensile strength of the composites were increased 64 and 27%, respectively, compared to the base metal. The reasons were studied in the light of reinforcing particles distribution, formation... 

Aluminum metal-matrix nanocomposites (AMMNCs) fabricated by conventional stir-casting process usually show high porosity and poor distribution of nanoparticles within the matrix. In the current study, for the improvement of nanoparticles distribution in the aluminum matrix and enhancement of the mechanical properties, a mixture of Al/nano-Al2O3 powders were injected by pure argon gas into the molten 7075 aluminum alloy and this mixture was extruded at high temperature. Mechanical behavior of the final product was investigated by tensile and compression tests, hardness measurements, Scanning Electron Microscopy (SEM), High Resolution Transmission Electron Microscopy (HRTEM) and Optical... 

Aluminum metal-matrix nanocomposites (AMMNCs) fabricated by conventional stir-casting process usually show high porosity and poor distribution of nanoparticles within the matrix. In the current study, for the improvement of nanoparticles distribution in the aluminum matrix and enhancement of the mechanical properties, a mixture of Al/nano-Al2O3 powders were injected by pure argon gas into the molten 7075 aluminum alloy and this mixture was extruded at high temperature. Mechanical behavior of the final product was investigated by tensile and compression tests, hardness measurements, Scanning Electron Microscopy (SEM), High Resolution Transmission Electron Microscopy (HRTEM) and Optical... 

4340 steel bars were austenitized at 850°C for 1 hour followed by heating at 700°C (ferrite and austenite region) for 90 min and quenching into a salt bath with different temperatures of 300, 350, 400 and 450°C. The steel bars were held for 1 hour at these temperatures before air cooling to room temperature. Various ferrite-bainite microstructures with 34% volume fraction of ferrite and different bainite morphologies were obtained. The results of SEM studies showed that by increasing the austempering temperature, the morphology of bainite varies from lower to upper bainite. According to the T-T-T diagram of the studied steel, the bainite transformation will not complete for the holding time... 

In this paper, the mechanical properties of graphene oxide are obtained using the molecular dynamics analysis, including the ultimate stress, Young modulus, shear modulus and elastic constants, and the results are compared with those of pristine graphene. It is observed that the increase of oxide agents (–O) and (–OH) leads to the increase of C–C bond length at each hexagonal lattice and as a result, alter the mechanical properties of the graphene sheet. It is shown that the elasticity modulus and ultimate tensile strength of graphene oxides (–O) and (–OH) decrease significantly causing the failure behavior of graphene sheet changes from the brittle to ductile. The results of shear loading...